Low-density polyethylene/LDPE particles for film and foam board applications

Description:             LLDPE / linear low density polyethylene virgin and recycle granules                1.Free Sample                2.SGS/CIQ Test     &nbs

Featured Products


Description:
             LLDPE / linear low density polyethylene virgin and recycle granules 
               1.Free Sample 
               2.SGS/CIQ Test 
               3.Factory Price/Quality
Specifications:
 
 
Film Grade
 

Tests

Value

Unit

Melt Flow Rate (MFR)

2.0±0.4

g/10min

Density

920±2

Kg/cm3

Tensile Strengthat Yield

8

Mpa ≥

Tensile Strengthat Break

12

Mpa ≥

haze

15

%≤

Packing

In 25 kg PP woven bags,20MT/20'FCL

 
 Master Batch Use  
 
 

Tests

Value

Unit

Melt Flow Rate (MFR)

20

g/10min

Density

0.924

g/cm3

Tensile Strength

MD12

Mpa

TD 10

Elongation at Yield

13

%

Elongation at Break

200

Dark Drop Impact

105

g

Brittle Temperature(F 50)

-70

°C

Vicat Softening Point

90

°C

Packing

In 25 kg wovenbags,20MT/20'FCL

 
 
Powder Rotational Molding Grade  
 
 

Tests

Value

Unit

Melt Flow Rate (MFR)

3.2

g/10min

Density

0.939

g/cm3

Melting Point

127

°C

Tensile Yield Strength

21

Mpa

Tensile Strength at Break

28

Mpa

Elongation at Break

1,100

%

Flexural Modulus

750

Mpa

Brittle Temperature

<-60

°C

 
 
 Application:
                      Make barrela, plastic bottle and bag, make all kind of pipes, make shading net, and make cable wire-insulating.
LLDPE Specifications:

PROPERTY

UNIT

Data

Melt Flow Index

g/10min

≤1.0

Density

g/cm3

≤0.945

Tensile strength 

Mpa

≥14.0

Elongation at break

%

≥600

Brittle temperature at low temperature

°C

≤-76

ESCR ,FO

H

≥500

Carbon Black dispersion

--

--

Tensile strength after thermal aging 

Mpa

≥13

Elongation after thermal aging

%

≥500

Dielectric strength

Mv/m

≥25

Volume resistivity

Ω.m

≥1*1014

change rate of tensile strength 
after weather aging environment of 0--1008h

%

±25

change rate of elongation
 after weather aging environment of 0--1008h

%

±25

change rate of tensile strength
 after weather aging environment of 504--1008h

%

±15

change rate of elongation
after weather aging environment of 504--1008h

%

±15

Contact us

Please feel free to give your inquiry in the form below We will reply you in 24 hours